Henkel Structural Bonding Solutions manual 3475 A&B 3479 A&B 3478 A&B 3474 A&B

	Aluminium	Metallic pieces under	Metallic pieces
		high compression	under friction
Multi purpose	High temperature	Putty	Wear resistant
	resistant
3475 A&B	3479 A&B	3478 A&B	3474 A&B
Metal Set A1	Metal Set HTA	Superior Metal	Metal Set M

2K-Epoxy	2K-Epoxy	2K-Epoxy	2K-Epoxy
1:1	1:1	4 :1	1:1
100 :100	100 :100	7.25 :1	100 :100
45 min.	40 min.	20 min.	45 min.
180 min.	150 min.	120 min.	180 min.
Grey	Grey	Dark grey	Grey
Putty	Putty	Putty	Putty
20 N/mm2	20 N/mm2	17 N/mm2	20 N/mm2
70 N/mm2	90 N/mm2	125 N/mm2	70 N/mm2
up to 120 °C	up to 190 °C	up to 120 °C	up to 120 °C
500 g tub kit	500 g tub kit	450 g tub kit	500 g tub kit

Loctite® Hysol® 3475 A&B Metal Set A1

•Aluminium putty

•Low shrinkage on cure (0.1 %)

•Temperature resistant (120 °C)

Loctite® Hysol® 3475 A&B is an aluminium filled, non-sagging, 2K-Epoxy adhesive for repairing and rebuilding worn metal parts. Ideal for repairing castings and cracks in housings and machine parts.

Loctite® Hysol® 3479 A&B Metal Set HTA

•Aluminium putty

•Low shrinkage on cure (0.2 %)

•High temperature resistant (190 °C)

Loctite® Hysol® 3479 A&B is an aluminium filled, non-sagging, 2K-Epoxy adhesive for repairing and rebuilding worn metal parts in high operating temperature applications. Ideal for repairing castings and cracks in housings and machine parts.

Loctite® Hysol® 3478 A&B Superior Metal

•Steel putty

•Low shrinkage on cure (0.1 %)

•High compression strength

•High temperature strength (120 °C)

Loctite® Hysol® 3478 A&B is a ferro-silicon filled, non-sagging, 2K-Epoxy adhesive, for repairing and rebuilding worn metal parts in areas under high compression loads. Ideal for shafts, bearing seats and parallel key assemblies.

Loctite® Hysol® 3474 A&B Metal Set M

•Self-lubricating

•High wear resistant

•Temperature resistant (120 °C)

Loctite® Hysol® 3474 A&B is a mineral filled, non-sagging,

2K-Epoxy adhesive which forms a self-lubricating surface to reduce sliding wear on moving parts. Ideal for metallic surfaces under friction.

15