(2/6)
FEATURES
•Large size ferrite cores developed for reactors and transformers used in high power units.
•Please contact us for machinability of
MATERIAL CHARACTERISTICS (Typical)
Material |
|
|
|
| PE22 | PC40 | |
Initial permeability | ∝i | [23°C] |
| 1800 | 2300 | ||
|
|
|
|
|
| ||
Curie temperature | Tc |
| °C | >200 | >200 | ||
|
|
|
|
|
| ||
Saturation magnetic flux density | Bs | [23°C] | mT | 510 | 500 | ||
H=1194A/m |
| [100°C] | 410 | 380 | |||
|
|
| |||||
|
|
|
|
|
| ||
Remanent flux density | Br | [23°C] | mT | 140 | 125 | ||
|
|
|
|
|
|
| |
Coercive force |
| Hc | [23°C] | A/m | 16 | 15 | |
|
|
|
|
|
|
| |
Core loss | 25kHz, 200mT | Pcv | [100°C] | kW/m3 | 80 | 70 | |
100kHz, 200mT | 520 | 420 | |||||
|
|
|
| ||||
|
|
|
|
|
| ||
Electrical resistivity | ρ |
| Ω • m | 3 | 6.5 | ||
|
|
|
|
|
| ||
Approximate density | dapp |
| kg/m3 | 4.8⋅ 103 | 4.8⋅ 103 | ||
Thermal expansion coefficient | α |
| 1/K | 12⋅ | 12⋅ | ||
Thermal conductivity | κ |
| W/mK | 5 | 5 | ||
|
|
|
|
|
|
| |
Specific heat |
| Cp |
| J/kg • K | 600 | 600 | |
|
|
|
|
|
| ||
Bending strength | δb3 |
| N/m2 | 9⋅ 107 | 9⋅ 107 | ||
Young’s modulus | E |
| N/m2 | 1.2⋅ 1011 | 1.2⋅ 1011 | ||
Magnetostriction |
| λs |
|
|
• 1(mT)=10(G),1(A/m)=0.012566(Oe)
CORE LOSS vs. TEMPERATURE CHARACTERISTICS
Pcv(kW/m3)
200
PE22
150
PC40
100
50
0
0 20 40 60 80 100 120 Temperature(˚C)
Pcv(kW/m3)
800
600
400
0
0
PE22
PC40
20 40 60 80 100 120 Temperature(˚C)
• All specifications are subject to change without notice.