Flux and Electrode Stabilizing Guide

	Air Conditioned	Dry Rod	After Exposure to Moisture a
Type (AWS)	Storage	Oven Holding	Sufficient Time to affect Weld Quality
	Before Opening	After Opening	Recondition	Rebake
			Step 1	Step 2
Standard			180°F ± 25°	240°F ± 25°
EXX10			two hours	one hour
EXX11	80°F ± 20°	140°F ± 30°
EXX12
	60% ± 10% RH
EXX13			Three hour total
EXX20
EXX30
Iron Powder	90°F ± 20°		180°F ± 25°	325°F ± 25°
EXX14		140°F ± 30°	two hours	one hour
EXX24	50% RH max		Three hour total
EXX27
Iron Powder-			180°F ± 25°	700°F ± 100°
Low Hydrogen	90°F ± 20°	400°F ± 50°	two hours	one-half hour
EXX18	50% RH max		Two & one-half hour total
EXX28
Low Hydrogen	90°F ± 20°		180°F ± 25°	600°F ± 100°
EXX15		400°F ± 50°	two hours	one-half hour
	50% RH max
EXX16			Two & one-half hour total
Low-Hydrogen			180°F ± 25°	700°F ± 100°
High Tensile	90°F ± 20°	400°F ± 50°	two hours	one-half hour
EXXX15	50% RH max		Two & one-half hour total
EXXX16
Stainless			180°F ± 25°	350°F ± 50°
Inconel
			one hour	one hour
Monel
	90°F ± 20°
Nickel		225°F ± 50°
Brasses	50% RH max
			Two hour total
Bronzes
Hard Surfacing
Special Alloys
Granulated or	90°F ± 20°	240° F ± 50°	Not required	700°F ± 100° ∅
Agglomerated
	50% RH max			two hours
Flux

IMPORTANT:

This table is offered as a guide to proper storage and oven holding temperatures for the most common electrodes in use today. In addition, recondition/rebake procedures for electrode coatings that have been exposed to moisture for a sufficient period of time to affect the weld quality are included. Good judgment and the manufacturer’s recommendations should be your guide.

Note: In the HTS Stainless electrode groups, and 15 & 16 type coatings, there can be a greater difference in the maximum temperature requirements for rebaking than those shown. This can be handled by special request to the particular manufacturer involved.

CONTACT YOUR ELECTRODE MANUFACTURER FOR SPECIFIC INFORMATION INVOLVING CRITICAL OPERATIONS.

Electrode coating should not be exposed to the rebaking temperature without first having been reconditioned at a lower temperature. Failure to observe this rule will result in breakdown of electrode coatings.

After rebake, lower temperature to holding level until reissue.