INTERNAL MATERIAL FLAW

This failure occurs when a foreign material is rolled into the steel during the manufacturing process, causing an imperfection in the internal material flaw grain. The re- sult is an inherent weakness in the tool shank and even- tual breakage.

The fatigue failure is started by the defects within the tool bit. The broken surface exhibits a shell pattern around the starting point of failure, like that in the fatigue failure. The other parts of the broken surface are brittle.

This is the only kind of tool bit failure that is always covered under warranty.

Figure 20. Internal Material Flaw

As a rule, working steel failures can be diagnosed by looking at the break itself, and at the place on the steel where the break occurred. Discoloration, like “rainbow” effects or blue bands, is the result of extreme heat.

Look for surface cracks, galling, or gouge marks. Breaks that start as surface damage have a “sea shell” pattern, with the damaged spot at the center. A large “sea shell” indicates a slow growing break; a small one indicates one compounded by side stress.

Stress failures start small, and spread into the center of the steel. In a stress failure, the coarser the grain, the greater the stress was, and the more rapid was the failure.

•Failures in this area are usually the result of blank firing, worn bushing(s), worn re- tainer pin(s) or the lack of lubrication.

•Failures in this area are usually the result of worn retainer pin(s) or blank firing.

•Failures in this area are usually the result of prying, metal-to-metal contact or corro- sion. Prying failures often exhibit a shell- like formation near the edge of the steel diameter where the break began, and a “tail” opposite that where the remaining steel bent and tore.

•Failures in this area are usually the result of heat build-up, mushrooming, or improp- er contact with the work.

Figure 21. Diagram of Tool Bit Failures

MBX15 User Manual ◄ 17

Page 16 Page 18
Image 17
Page 16 Page 18
Contents MBX15 MBX15Read Wear Eye Manual Protection Hearing Breathing Table of Contents General Safety Precautions Safety PrecautionsSafety Precautions Local Safety Regulations Safety SymbolsMBX15 Tool DecalsPreparation for Operation PRE-INSTALLATION InstructionsPRE-OPERATION Long Term Storage LOW-TEMPERATURE WARM-UP ProcedureSecuring the Tool Preparation for USE OperationPositioning the Excavator Positioning the Breaker Tool on the Work MaterialBreaker Binding BreakingBlank Firing Underwater USE Underwater USETool Stop & Lower Bushing Periodic Maintenance ChecksEach DAY WORN-OUT Front Bushings or Retainer Pins Tool Failure not Covered Under WarrantyProper USE & Care of Tool Bits Blank Firing or Free RunningCorrosion PryingInternal Material Flaw Tool Failure Covered Under WarrantyBlunt MoilChisel Problem Cause Solution TroubleshootingCharging the Main Accumulator When disengaging the tester a POP of nitrogen is normalRecommended Torque Values Recommended Tie Rod Torque ProcedureHeat Load Test Flow Test ProceduresTest Procedure Accessories SpecificationsMBX15 Power Cell Illustration QTY Description MBX15 Power Cell Parts ListMBX15 Housing Parts Hydraulic Tools Declaration of Conformity

MBX15 specifications

The Stanley Black & Decker MBX15 is a robust and versatile tool designed for professionals and serious DIY enthusiasts alike. Engineered to meet the needs of various applications, this machine stands out in the crowded marketplace of power tools, providing exceptional reliability and performance.

At the heart of the MBX15 is its powerful motor, which delivers impressive torque and speed, enabling users to tackle a wide range of tasks with ease. The efficiency of this motor allows for quick job completion without sacrificing quality. One of the standout features of the MBX15 is its lightweight design, making it easy to handle during extended use. The ergonomically designed handle ensures maximum comfort, reducing fatigue and enhancing user control.

The MBX15 incorporates advanced technologies that set it apart from its competitors. For instance, it features an innovative vibration-dampening system that minimizes user discomfort. This technology is especially beneficial during prolonged operations, allowing for greater precision and fewer errors. Additionally, the tool is equipped with a quick-change system, enabling users to switch attachments seamlessly, thus enhancing productivity.

A distinctive characteristic of the MBX15 is its versatility. It comes with a variety of attachments specifically designed for different applications such as grinding, polishing, and even surface preparation. This multifunctionality makes it an essential addition to any workshop or job site.

The MBX15 also prioritizes safety, incorporating several features to protect users during operation. The integrated safety switch prevents accidental start-ups, and the durable housing safeguards the internal components, ensuring longevity and reliability even in demanding environments.

In terms of design aesthetics, the MBX15 boasts a sleek and modern look, complete with a sturdy build that reflects the quality synonymous with the Stanley Black & Decker brand. This tool not only delivers on performance but also complements the professionalism of its users.

In conclusion, the Stanley Black & Decker MBX15 is a formidable tool equipped with a powerful motor, innovative technologies, and a user-friendly design. Its versatility, coupled with safety features and comfort, makes it an exceptional choice for any project, whether on a professional job site or at home. With its blend of power and efficiency, the MBX15 is truly a reliable partner for all your grinding and surface preparation needs.
Top Page Image Contents