Hobart Welding Products 4500 manual Weld Test, Troubleshooting − Porosity, Possible Causes

12-13. Weld Test

2 To 3 in

(51-76 mm)

1/4 in (6.4 mm)

3
	3
	2 To 3 in
	(51-76 mm)
2	2
1	1

1Vise

2Weld Joint

3Hammer

Strike weld joint in direction shown. A good weld bends over but does not break.

S-0057-B

12-14. Troubleshooting − Porosity

Porosity − small cavities or holes resulting from gas pockets in weld metal.

Possible Causes	Corrective Actions
Arc length too long.	Reduce arc length.
Damp electrode.	Use dry electrode.
Workpiece dirty.	Remove all grease, oil, moisture, rust, paint, coatings, slag, and dirt from work surface before
	welding.

12-15. Troubleshooting − Excessive Spatter

Excessive Spatter − scattering of molten metal particles that cool to solid form near weld bead.

Possible Causes	Corrective Actions
Amperage too high for electrode.	Decrease amperage or select larger electrode.
Arc length too long or voltage too high.	Reduce arc length or voltage.

OM-4418 Page 42