Hobart Welding Products 175 manual Troubleshooting − Excessive Spatter, Troubleshooting − Porosity

Page 40

8-8.

Troubleshooting − Excessive Spatter

 

 

Excessive Spatter − scattering of molten metal particles that

 

 

cool to solid form near weld bead.

 

 

S-0636

 

Possible Causes

Corrective Actions

Wire feed speed too high.

Select lower wire feed speed.

Voltage too high.

Select lower voltage range.

Electrode extension (stickout) too long.

Use shorter electrode extension (stickout).

Workpiece dirty.

Remove all grease, oil, moisture, rust, paint, undercoating, and dirt from work surface before welding.

Insufficient shielding gas at welding arc.

Increase flow of shielding gas at regulator/flowmeter and/or prevent drafts near welding arc.

Dirty welding wire.

Use clean, dry welding wire.

 

 

Eliminate pickup of oil or lubricant on welding wire from feeder or liner.

8-9.

Troubleshooting − Porosity

 

 

Porosity − sm all cavities or holes resulting from gas pockets

 

 

in weld metal.

 

 

S-0635

 

Possible Causes

Corrective Actions

Insufficient shielding gas at welding arc.

Increase flow of shielding gas at regulator/flowmeter and/or prevent drafts near welding arc.

 

 

Remove spatter from gun nozzle.

 

 

Check gas hoses for leaks.

 

 

Place nozzle 1/4 to 1/2 in (6-13 mm) from workpiece.

 

 

Hold gun near bead at end of weld until molten metal solidifies.

Wrong gas.

Use welding grade shielding gas; change to different gas.

Dirty welding wire.

Use clean, dry welding wire.

 

 

Eliminate pick up of oil or lubricant on welding wire from feeder or liner.

Workpiece dirty.

Remove all grease, oil, moisture, rust, paint, coatings, and dirt from work surface before welding.

 

 

Use a more highly deoxidizing welding wire (contact supplier).

Welding wire extends too far out of nozzle.

Be sure welding wire extends not more than 1/2 in (13 mm) beyond nozzle.

8-10. Troubleshooting − Excessive Penetration

Excessive Penetration − weld metal melting through base metal and hanging underneath weld.

Excessive Penetration Good Penetration

S-0639

Possible Causes

Corrective Actions

Excessive heat input.

Select lower voltage range and reduce wire feed speed.

 

Increase travel speed.

OM-944 Page 36

Return To Table Of Contents

Page 39 Page 41
Image 40
Page 39 Page 41
Contents Processes OM-944Description From Hobart to You Table of Contents Options and Accessories Warranty Symbol Usage Marks a special safety messageArc Welding Hazards Electric Shock can killARC Rays can burn eyes and skin Welding can cause fire or explosionFlying Metal can injure eyes Buildup of GAS can injure or killCalifornia Proposition 65 Warnings EMF Information Principal Safety StandardsAbout Pacemakers Identifie un message de sécurité particulier − Consignes DE Sécurité − À Lire Avant UtilisationLE Soudage peut causer un incen- die ou une explosion LES Particules Projetées peu- vent blesser les yeuxLES Pièces Chaudes peuvent cau- ser des brûlures graves LE Bruit peut affecter l’ouïeRisque D’INCENDIE OU D’EXPLO LA Chute DE L’APPAREIL peut blesser’EMPLOI Excessif peut Faire LES Pièces Mobiles peuvent cau- ser des blessuresInformation sur les champs électromagnétiques Principales normes de sécuritéConsignes relatives aux stimulateurs cardiaques Specifications − SpecificationsVAC Model Duty Cycle And Overheating OutputDuty Cycle % Output AmperesVolt-Ampere Curves Load Amps− Installation Installing Welding Gun Installing Work ClampProcess/Polarity Table Changing PolarityInstalling Gas Supply Rating Label Do not move or operate unit where it could tip = GND/PEElectrical Service Guide For 230 VAC Model Installing Wire Spool And Adjusting Hub TensionThreading Welding Wire Hold wire tightly to keep it from unraveling− Operation ControlsWeld Parameter Chart For 115 VAC Model Welding GuideFor 115 Volt Wire Welding Package Weld Parameter Chart For 230 VAC Model For 230 Volt Wire Welding Package − Maintenance &TROUBLESHOOTING Routine MaintenanceDisconnect power before maintaining Overload Protection Drive Motor ProtectionTurn Off power before replacing contact tip Changing Drive Roll Or Wire Inlet GuideReplacing Gun Contact Tip Disconnect gun from unit Cleaning Or Replacing Gun LinerTo Reassemble Gun Replacing Switch And/Or Head Tube Troubleshooting Table Trouble Remedy− Electrical Diagram Circuit Diagram For 115 VAC ModelCircuit Diagram For 230 VAC Model − MIG Welding Gmaw Guidelines Typical MIG Process ConnectionsTypical MIG Process Control Settings Wire Size Amperage RangeThickness to Amperage a Select VoltageHolding And Positioning Welding Gun Conditions That Affect Weld Bead Shape Good Weld Bead Characteristics Poor Weld Bead CharacteristicsGun Movement During Welding Troubleshooting − Excessive Spatter Troubleshooting − PorosityTroubleshooting − Excessive Penetration Possible Causes Corrective ActionsTroubleshooting − Incomplete Fusion Troubleshooting − Lack Of PenetrationTroubleshooting − Burn-Through Troubleshooting − Waviness Of Bead Troubleshooting − DistortionCommon MIG Shielding Gases Troubleshooting Guide For Semiautomatic Welding EquipmentApplication Welding arc not stable Wire slipping in drive rolls Return To Table Of Contents − Parts List Main AssemblyDia Part H-10 Gun Options Optional Drive Rolls195 Page Service SupportContact your Distributor for Hobart Welding Products
Top Page Image Contents