Miller Electric H-10, MW 140 Plus Troubleshooting − Excessive Spatter, Troubleshooting − Porosity

Page 37

9-8.

Troubleshooting − Excessive Spatter

 

 

Excessive Spatter − scattering of molten metal particles that

 

 

cool to solid form near weld bead.

 

 

S-0636

 

Possible Causes

Corrective Actions

Wire feed speed too high.

Select lower wire feed speed.

Voltage too high.

Select lower voltage range.

Electrode extension (stickout) too long.

Use shorter electrode extension (stickout).

Workpiece dirty.

Remove all grease, oil, moisture, rust, paint, undercoating, and dirt from work surface before welding.

Insufficient shielding gas at welding arc.

Increase flow of shielding gas at regulator/flowmeter and/or prevent drafts near welding arc.

Dirty welding wire.

Use clean, dry welding wire.

 

 

Eliminate pickup of oil or lubricant on welding wire from feeder or liner.

Incorrect polarity.

Check polarity required by welding wire, and change to correct polarity at welding power source.

9-9.

Troubleshooting − Porosity

 

 

Porosity − small cavities or holes resulting from gas pockets

 

 

in weld metal.

 

 

S-0635

 

Possible Causes

Corrective Actions

Insufficient shielding gas at welding arc.

Increase flow of shielding gas at regulator/flowmeter and/or prevent drafts near welding arc.

 

 

Remove spatter from gun nozzle.

 

 

Check gas hoses for leaks.

 

 

Place nozzle 1/4 to 1/2 in (6-13 mm) from workpiece.

 

 

Hold gun near bead at end of weld until molten metal solidifies.

Wrong gas.

Use welding grade shielding gas; change to different gas.

Dirty welding wire.

Use clean, dry welding wire.

 

 

Eliminate pick up of oil or lubricant on welding wire from feeder or liner.

Workpiece dirty.

Remove all grease, oil, moisture, rust, paint, coatings, and dirt from work surface before welding.

 

 

Use a more highly deoxidizing welding wire (contact supplier).

Welding wire extends too far out of nozzle.

Be sure welding wire extends not more than 1/2 in (13 mm) beyond nozzle.

9-10.

Troubleshooting − Excessive Penetration

 

 

Excessive Penetration − weld metal melting through base metal

 

 

and hanging underneath weld.

 

Excessive Penetration Good Penetration

 

 

S-0639

 

Possible Causes

Corrective Actions

Excessive heat input.

Select lower voltage range and reduce wire feed speed.

 

 

Increase travel speed.

 

 

OM-219 316 Page 33

Page 36 Page 38
Image 37
Page 36 Page 38
Contents Processes OM-219 316C→Description 2006−10Page Table of Contents − Parts List Marks a special safety message Symbol UsageArc Welding Hazards Electric Shock can killWelding can cause fire or explosion ARC Rays can burn eyes and skinFlying Metal can injure eyes Buildup of GAS can injure or killCalifornia Proposition 65 Warnings EMF Information Principal Safety StandardsAbout Pacemakers LES Fumées ET LES GAZ peuvent être dangereux UNE Décharge Électrique peut entraîner la mortIndique un message de sécurité particulier Incendie ou une explosion LE Soudage peut provoquer unDES Particules Volantes peuvent blesser les yeux DES Pièces Chaudes peuvent provoquer des brûlures gravesLA Chute DE L’APPAREIL peut blesser Risque D’INCENDIE OU D’EXPLO’EMPLOI Excessif peut SUR DES Organes Mobiles peuvent provoquer des blessuresEn ce qui concerne les stimulateurs cardiaques Principales normes de sécuritéSymbols And Definitions − SpecificationsSpecifications − DefinitionsDuty Cycle And Overheating WarrantyOutput Duty Cycle % Exceeding duty cycle canAmperage Volt-Ampere CurvesInstalling Welding Gun − InstallationIncorrect CorrectChanging Polarity Process/Polarity TableCO 2 gas regulator/flowmeter Installing Gas SupplyDo not move or operate unit where it could tip Selecting a Location And Connecting Input PowerInstalling 8 in 203 mm Wire Spool Installing Wire Spool And Adjusting Hub TensionFlux Nozzle Installing Contact Tip And NozzleHold wire tightly to keep it from unraveling Threading Welding WireControls − OperationWeld Parameter Chart 217 618-A Routine Maintenance − Maintenance &TROUBLESHOOTINGOverload Protection Drive Motor ProtectionTurn Off power before replacing contact tip Changing Drive Roll Or Wire Inlet GuideReplacing Gun Contact Tip Disconnect gun from unit Cleaning Or Replacing Gun LinerTo Reassemble Gun Replacing Switch And/Or Head Tube Trouble Remedy Troubleshooting TableDoes not run Circuit Diagram − Electrical DiagramTypical MIG Process Connections − MIG Welding Gmaw GuidelinesWire Size Amperage Range Typical MIG Process Control SettingsThickness to Amperage a Select VoltageHolding And Positioning Welding Gun Conditions That Affect Weld Bead Shape Good Weld Bead Characteristics Poor Weld Bead CharacteristicsGun Movement During Welding Troubleshooting − Porosity Troubleshooting − Excessive SpatterTroubleshooting − Excessive Penetration Possible Causes Corrective ActionsTroubleshooting − Incomplete Fusion Troubleshooting − Lack Of PenetrationTroubleshooting − Burn-Through Troubleshooting − Distortion Troubleshooting − Waviness Of BeadWire does not feed Troubleshooting Guide For Semiautomatic Welding EquipmentCommon MIG Shielding Gases ApplicationWelding arc not stable Wire slipping in drive rolls Main Assembly − Parts ListDia Part Description Quantity Dia Part Description Quantity Mkgs 195 H-10 GunOptions Optional Drive RollsWarranty Owner’s Record